Tengbo Ma#, Yongsheng Zhao#, Kunpeng Ruan, Xirui Liu, Junliang Zhang, Yongqiang Guo, Xutong Yang, Jie Kong and Junwei Gu*. Highly Thermal Conductivities, Excellent Mechanical Robustness and Flexibility, and Outstanding Thermal Stabilities of Aramid Nanofiber Composite Papers with Nacre-Mimetic Layered Structures. ACS Applied Materials & Interfaces, 2020, 12(1): 1677-1686. (SCI: 000507146100171; Ei: 20200207988167) 2020IF=9.229.(1区材料科学Top期刊)ESI高被引论文(2020年第4~6期,2021年第1~6期,2022年第1~2期)
以芳纶纳米纤维(ANF)为基体、聚多巴胺(PDA)改性的氮化硼纳米片(BNNS@PDA)为导热填料,通过真空抽滤法制备BNNS@PDA/ANF导热复合纸。结果表明,BNNS@PDA/ANF导热复合纸的面间导热系数(λ⊥)和面内导热系数(λ∥)均随BNNS用量增加而提高。相同BNNS用量下,表面功能化改性有助于进一步提高BNNS/ANF导热复合纸的导热性能和力学性能。当BNNS用量为50 wt%时,BNNS@PDA/ANF导热复合纸的面间导热系数(λ⊥)和面内导热系数(λ∥)分别达到0.62 W/mK和3.94 W/mK,均分别高于相同BNNS用量(50 wt%)的BNNS/ANF导热复合纸的λ⊥(0.52 W/mK)和λ∥(3.33 W/mK),并较纯ANF纸的λ⊥(0.22 W/mK)和λ∥(1.33 W/mK)分别提高了181.8%和196.2%;同时,BNNS@PDA/ANF导热复合纸的拉伸强度为36.8 MPa,比相同BNNS用量(50 wt%)BNNS/ANF导热复合纸(28.2 MPa)提高了30.3%。另外,BNNS@PDA/ANF复合纸具有优异的热稳定性(最大热分解温度 Tmax>500℃)。本文制备的BNNS@PDA/ANF导热复合纸具有良好的导热性能、理想的力学性能和优异热稳定性,在柔性可穿戴设备、电子产品等领域具有潜在的应用价值。
论文下载:Highly Thermal Conductivities, Excellent Mechanical Robustness and Flexibility, .pdf
论文链接:https://doi.org/10.1021/acsami.9b19844
Archiver|手机版|科学网 ( 京ICP备07017567号-12 )
GMT+8, 2024-4-30 21:47
Powered by ScienceNet.cn
Copyright © 2007- 中国科学报社