     Silicon Carbide is the only chemical compound of carbon and silicon. It was originally produced by a high temperature electro-chemical reaction of sand and carbon. Silicon carbide is an excellent abrasive and has been produced and made into grinding wheels and other abrasive products for over one hundred years. Today the material has been developed into a high quality technical grade ceramic with very good mechanical properties. It is used in abrasives, refractories, ceramics, and numerous high-performance applications. The material can also be made an electrical conductor and has applications in resistance heating, flame igniters and electronic components. Structural and wear applications are constantly developing.

.Key Silicon Carbide Properties
Low density
High strength
Low thermal expansion
High thermal conductivity
High hardness
High elastic modulus
Excellent thermal shock resistance
Superior chemical inertness
.
Silicon Carbide Typical Uses
Fixed and moving turbine components
Suction box covers
Seals, bearings
Ball valve parts
Hot gas flow liners
Heat exchangers
Semiconductor process equipment
General Silicon Carbide Information     Silicon carbide is composed of tetrahedra of carbon and silicon atoms with strong bonds in the crystal lattice. This produces a very hard and strong material. Silicon carbide is not attacked by any acids or alkalis or molten salts up to 800. In air, SiC forms a protective silicon oxide coating at 1200 and is able to be used up to 1600. The high thermal conductivity coupled with low thermal expansion and high strength give this material exceptional thermal shock resistant qualities. Silicon carbide ceramics with little or no grain boundary impurities maintain their strength to very high temperatures, approaching 1600 with no strength loss. Chemical purity, resistance to chemical attack at temperature, and strength retention at high temperatures has made this material very popular as wafer tray supports and paddles in semiconductor furnaces. The electrical conduction of the material has lead to its use in resistance heating elements for electric furnaces, and as a key component in thermistors (temperature variable resistors) and in varistors (voltage variable resistors).
Download Silicon Carbide datasheet
Silicon Carbide Engineering Properties*
Silicon Carbide Properties
Mechanical
SI/Metric (Imperial)
SI/Metric
(Imperial)
Density
gm/cc (lb/ft3)
3.1
(193.5)
Porosity
% (%)
0
(0)
Color
black
Flexural Strength
MPa (lb/in2x103)
550
(80)
Elastic Modulus
GPa (lb/in2x106)
410
(59.5)
Shear Modulus
GPa (lb/in2x106)
Bulk Modulus
GPa (lb/in2x106)
Poisson’s Ratio
0.14
(0.14)
Compressive Strength
MPa (lb/in2x103)
3900
(566)
Hardness
Kg/mm2
2800
Fracture Toughness KIC
MPa•m1/2
4.6
Maximum Use Temperature
(no load)
癈 (癋)
1650
(3000)
Thermal



Thermal Conductivity
W/m•癒 (BTU•in/ft2•hr•癋)
120
(830)
Coefficient of Thermal Expansion
10–6/癈 (10–6/癋)
4.0
(2.2)
Specific Heat
J/Kg•癒 (Btu/lb•癋)
750
(0.18)
Electrical



Dielectric Strength
ac-kv/mm (volts/mil)
semiconductor
Dielectric Constant
Dissipation Factor
Loss Tangent
Volume Resistivity
ohm•cm
102–106
dopant dependent
*All properties are room temperature values except as noted.
The data presented is typical of commercially available material and is offered for comparative purposes only. The information is not to be interpreted as absolute material properties nor does it constitute a representation or warranty for which we assume legal liability. User shall determine suitability of the material for the intended use and assumes all risk and liability whatsoever in connection therewith.


References:
http://accuratus.com/silicar.html

回复

使用道具 举报

发表于 2015-10-14 09:03:22 | 显示全部楼层
顶一个
回复 支持 反对

使用道具 举报

发表于 2015-6-21 19:38:59 | 显示全部楼层
非常实用
回复 支持 反对

使用道具 举报

发表于 2012-2-23 10:08:13 | 显示全部楼层
不错   就是有些乱码
回复 支持 反对

使用道具 举报

Archiver|手机版|小黑屋|科学网 ( 京ICP备14006957 )

GMT+8, 2017-9-20 08:09

Powered by ScienceNet.cn

Copyright © 2007-2017 中国科学报社

快速回复 返回顶部 返回列表